ELASTOSIL® R plus 4806/20 MH

HTV silicone rubbers of the grade ELASTOSIL® R plus 4806/20 MH are oil-bleeding one-component platinum-curing compounds for the manufacture of molded articles. The vulcanizates form a thin oil film with lubricationg properties shortly after the curing process. As the crosslinking system is based on platinum cure no peroxide decomposition products can be formed during curing.



Eigenschaften

ELASTOSIL® R plus 4806/20 MH is a fast curing silicone rubber exhibiting excellent cut resistance. Thanks to addition cure, the vulcanization reaction is significantly faster compared to peroxide curing materials. No peroxide decomposition products are formed during vulcanization.

 

The addition of heat stabilizers at service temperatures of more than 180 °C is recommended.

 

Further information about an improvement of the heat stability by use of specific ELASTOSIL® AUX Heat Stabilizers can be obtained from the Technical Information Sheet "ELASTOSIL® AUX Stabilizers H" or the latest edition of our brochures.

Spezifische Merkmale von ELASTOSIL® R plus 4806/20 MH

  • Spezifische Merkmale: Additionsvernetzend
  • Spezifische Merkmale: einkomponentig
  • Spezifische Merkmale: ölausschwitzend
  • Vernetzungseigenschaft: Additionsvernetzend
  • Vernetzungseigenschaft: einkomponentig

Disclaimer

Alle unsere Angaben beruhen auf bestem Wissen. Allerdings übernehmen wir hierfür keine Haftung oder Gewährleistung und behalten uns jederzeit technische Änderungen vor. Es liegt in der eigenen Verantwortung des Käufers, die Angaben sowie die Geeignetheit unseres Produktes für den vorgesehenen Einsatzzweck vor dem Gebrauch zu überprüfen. Vertragliche Regelungen gehen immer vor. Der Gewährleistungs- und Haftungsausschluss gilt - insbesondere im Ausland - auch im Hinblick auf Schutzrechte Dritter.

ELASTOSIL® R plus 4806/20 MH is suitable for the manufacture of molded articles like multi cavity seals for technical applications. Specially thick walled articles can take advantage of this fast curing material.

This material can be processed on conventional silicone rubber injection molding equipment. Caution, danger of de- activation! The platinum catalyst can be de-activated already by amines or sulphur components in the air.

 

For detailed information please refer to the latest edition of our brochure "SOLID AND LIQUID SILICONE RUBBER - MATERIAL AND PROCESSING GUIDELINES".

Verpackung / Gebinde

This product is available in 20 kg cardboard packaging.

Lagerung

Once opened, cardboard boxes should always be resealed after use to prevent the platinum catalyst from being poisoned by amines, sulphur or phosphorus compounds. The 'Best use before end' date of each batch is shown on the product label. Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

Vertrieb & Support

Wacker Chemie AG
Heilbronner Strasse 74
70191 Stuttgart
Deutschland
+49  711  61942-0 (Phone)
+49 711 61942-61  (Fax)
Kontakt

Wie können wir Ihnen helfen?

  • Benötigen Sie Unterstützung bei der Produktauswahl oder wünschen Sie eine technische Beratung? Kontaktieren Sie unsere Experten.
Frage stellen

Sie möchten ein Produktmuster?

Hier können Sie ein Produktmuster anfordern.

Muster anfordern

Mehr Produkte

Produkte Technische Daten
Härte Shore A Reißfestigkeit Reißdehnung Weiterreißwiderstand Druckverformungsrest
ELASTOSIL® R plus 4806/20 MH 23[1] 23[1] 6,3 N/mm²[2] 6,3 N/mm²[2] 880 %[3] 880 %[3] 15 N/mm[4] 15 N/mm[4] 14 %[5] 14 %[5]
ELASTOSIL® R plus 4846/30 MH 30[1] 30[1] 10,8 N/mm²[2] 10,8 N/mm²[2] 1100 %[3] 1100 %[3] 34 N/mm[4] 34 N/mm[4] 19 %[5] 19 %[5]
Legend
[1] Härte Shore A | DIN ISO 48-4,  [2] Reißfestigkeit | ISO 37 Type 1,  [3] Reißdehnung | ISO 37 Type 1,  [4] Weiterreißwiderstand | ASTM D 624 B,  [5] Druckverformungsrest | 22 h | 175 °C | DIN ISO 815-1 Typ B Methode A | post-cured 4 h / 200 °C 