VINNAPAS® EAF 730 is a polymer dispersion based on vinyl ester, ethylene and acrylic acid ester. It is characterized by its very good hydrophobic properties combined with an excellent color stability.


  • Excellent cost-in-use compared to alternative high-end technologies
  • Perfectly spans all PVC levels (30% – 90%)
  • Very good hydrophobicity
  • Outstanding color stability and compatibility even with sensitive organic pigments
  • Higher inherent flame retardancy than standard acrylic systems
  • Very good film-forming properties
  • Very good scrub resistance
  • High blocking resistance
  • Very low dirt pick-up
  • Excellent saponification resistance
  • Very good compatibility with cement
  • Produced without the use of APEOs

The principal feature of VINNAPAS® EAF 730 is its wide range of uses in coating systems containing opacifying pigments. Versatility is its special strength.


VINNAPAS® EAF 730 is particularly recommended to produce masonry paints with good hiding power and great flexibility.

Thanks to its good resistance to saponification, VINNAPAS® EAF 730 can be employed as the organic polymer component of organo-silicate paints and renders. To ensure a good shelf life, the formulation must be carefully built around the binder.

Due to its minimum film forming temperature of approx. +3°C VINNAPAS® EAF 730 does not need any coalescing aids for filming, thus it is a very suitable binder for paints which complies with the criteria of tighter environmental-labels.

VINNAPAS® EAF 730 has proved itself as an excellent binder for resin bound plasters, especially in external thermal insulation composite systems with rendering (ETICS). In such a system, VINNAPAS® EAF 730 can also be used as binder for the base coat. Hence, only one binder is needed for the entire system.

The dispersion is readily compatible with Portland cement and its setting behavior is hardly influenced. As a consequence, water resistance of the base coat can be increased.

Due to the low calorific value of VINNAPAS® EAF 730, correctly installed ETICS with this composition fall under Fire Class A2 as per EN 13501.

VINNAPAS® EAF 730 is also a suitable binder for silicone resin emulsion paints (SREP) as well silicone renders.


Please discuss additional applications with your WACKER customer representative.


If the product is used in applications other than those mentioned, the choice, processing and use of the product is the sole responsibility of the purchaser. All legal and other regulations must be complied with.

For questions concerning food contact status according the chapter 21 CFR (US FDA) and German BfR, please feel free to contact us.

Wacker Chemie AG
Hanns-Seidel-Platz 4
D-81737 München


Non-returnable PE drums of 150 kg capacity (standard dispatch quantity: only fully-loaded pallets à 750 kg), non-returnable containers of 1 t capacity and road tankers.


When the dispersion is stored in tanks, proper storage conditions must be maintained. The product has a shelf life of 6 months starting from the date of receipt if stored in the original, unopened containers at temperatures between 5 and 30 °C. Any longer periods for the maximum storage period that may be described in the Certificate of Analysis which accompanies each shipment of the product, take preference over this suggestion in which case the time period stated in the Certificate of Analysis shall be solely authoritative. Iron or galvanized iron containers and equipment are not recommended. Corrosion could result in discoloration of the dispersion or blends made from it in further processing. We therefore recommend the use of containers and equipment made of ceramic, rubberized or enameled materials, appropriately finished stainless steel, or plastic (rigid PVC, polyethylene or polyester resin). As polymer dispersions may tend to superficial film formation, skins or lumps may be formed during storage or transportation. A filtration process is thus recommended prior to utilization of the product.

Preservation for Transport, Storage and further Processing

The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package.

Measures should also be taken to ensure cleanliness of the tanks and pipes. In unstirred tanks, a layer of preservative-containing water should be sprayed onto the surface of the dispersion to prevent the formation of unwanted skin and possible attack by microorganisms. The thickness of this water layer should be < 5 mm for low viscosity dispersions and up to 10–20 mm for high viscosity products. Proper procedures – periodic tank cleaning and sanitization – must be set up in order to prevent microbial attack. Contact your biocide representative/supplier for further plant hygiene recommendations. Measures should be taken to ensure that only clean air enters the tank when the dispersion is removed.

Finished products manufactured from polymer dispersions usually also require preservation. The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required.

Sales and support

Wacker Chemical Corporation
6870 Tilghman St
Allentown, PA 18106-9346
United States
+1  610  336-2700 (Phone)
+1 517 264-4088  (Fax)

How can we help you?

  • Do you need help in choosing a product or do you require technical support? If so, please contact our experts.
Ask a question


My media

My favorites

My products