POWERSIL® GEL FC A/B
POWERSIL® GEL FC A/B is a pourable, addition-curing, two-component silicone mixture that vulcanizes at room temperature to a soft silicone gel. POWERSIL® GEL FC A/B shows a very fast curing behavior.
- two-part, 1 : 1 mixing ratio
- very low viscosity (uncured)
- very low hardness (silicone gel)
- transparent vulcanizate
- excellent mechanical damping properties
- non-bleeding gel
POWERSIL® GEL FC A/B的特殊性能
- 具体特征: 快速固化
- sealing of MV and HV cable joints
- LV easy-to-use cable joints
- castings and sealants of electrical equipment
The platinum catalyst is contained in component B. Only components A and B with the same lot number may be processed together.
All surfaces must be clean and free of contaminants that will inhibit the cure of POWERSIL® GEL FC A/B. Examples of inhibiting contaminants are sulfur containing materials, plasticizers, urethanes, amine containing materials and organometallic compounds especially organo-tin compounds. If a substrate’s ability to inhibit curing is unknown, a small scale test should be run to determine compatibility.
The two components should be thoroughly mixed at a 1 : 1 ratio by weight or volume. To eliminate any air introduced during dispensing or trapped under components or devices a vacuum encapsulation is recommended.
The reactivity can be adjusted within wide limits by adding Catalyst EP or Inhibitor PT 88 to suit the processing requirements of the particular application. Catalyst EP increases the reactivity of the gel with corresponding reduction or pot life and curing time. Further information is given in our leaflet “Catalyst EP/Inhibitor PT 88”.
If the gel is too soft and tacky, reducing the amount of component B will result in a harder, less tacky vulcanizate. The hardest formulation is achieved with a mixing ratio for A : B of roughly 1.5 : 1.
We recommend running preliminary tests to optimize conditions for the particular application.
Comprehensive processing instructions are given in our leaflet “Wacker RTV-2 Silicone RubberProcessing”
POWERSIL® GEL FC A/B can be pigmented by adding 1 - 4 % of an ELASTOSIL® FL pigment paste.
Curing time of addition curing silicone rubber is highly dependent on temperature, size and heat sink properties of the component being potted.
The 'Best use before end' date of each batch is shown on the product label.
Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.