POWERSIL® 567 is a one-component silicone dispersion that cures to a tough high voltage insulator coating with very good electrical properties.
- very good resistance to weathering
- outstanding tracking resistance
POWERSIL® 567 的特殊性能
- 具体特征: 优异的疏水性
Protective silicone coating for procelain, glass and epoxy insulators as well as for other high-voltage insulating equipment where surface contamination causes service problems.
POWERSIL® 567 forms a long-term hydrophobic surface. Thus it prevents the formation of wet conductive films and therefore the risk of pollution flashovers.
The insulator surface to be coated should be clean and free of dust and grease. For cleaning the following operations are suggested:
- Proper cleaning by using water and a suitable detergent might be sufficient.
- Insulators that show an adhering pollution, such like cement, other mineral or chemical pollution layers should be cleaned by either "cob corn-" or carbon dioxide blasting.
- Any type of grease or fatty pollution is to be removed by using a suitable solvent like benzine or turpentine.
- Residual contaminants should be removed by thoroughly wiping.
- Finish the cleaning just before spraying POWERSIL® 567 with Isopropanol or an equivalent alcohol.
Check carefully that there is no of dirt or grease left before spraying!
In most cases it is not necessary to apply a primer before coating.
Proper stirring is recommended before the material is used.
POWERSIL® 567 is preferably applied by spraying. It can be applied by brushing or dipping as well. For spraying application, the airless process was found to be efficient. The following equipment settings were found to be suitable:
- Flat nozzle of 0,33 mm, 20°,
- Setting of pressure output 50 - 150 bar.
The spray gun should be moved evenly across the surface at a distance of about 30 - 50 cm. Due to the thixotropic properties of POWERSIL® 567 it is usually possible to apply the first layer with a good cover. A second layer can be applied after approximately 30 minutes.
A typical dry film thickness is 0,4 mm to 0,5 mm. Thus, the theoretical consumption is 1,3 kg to 1,7 kg of POWERSIL® 567 per square meter of insulator surface. Take losses for overspray and cleaning of the equipment into consideration.
Rain can damage the coating. In case of rain, please protect the job site or stop application.
Full cure is obtained in 8 – 12 hours after coating application depending on thickness, temperature and humidity.
All spraying equipment should be cleaned with a nonpolar solvent (e. g. Xylene or White Spirit) immediately after use.
The product contains migratable matter that is able to encapsulate contaminants and to provide a hydrophobic surface. Coated insulators may appear dirty after some time in service. Nevertheless, washing and cleaning, especially with detergents and other chemicals is not recommended.
The water repellent appearance can be evaluated by spraying with water. IEC 62073, “Guidance on the measurement of wettability of insulator surfaces” provides further information. A partly lowering of the effect does not necessarily require immediate action. Experience shows that the remaining parts of the insulator will provide the necessary insulation ability.
Physical damage, such like scratching can be easily repaired by brushing of fresh coating after partly cleaning with benzine.
To allow an instant replacement of broken insulators it is recommendable to store a number of coated spare insulators. These should be stored in a protective covering.
The 'Best use before end' date of each batch is shown on the product label.
Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.
|Tear-growth resistance||动态粘度||Shore density A||Breaking strength||断裂伸长率|
|POWERSIL® 567||9.0 N/mm 9.0 N/mm||1400 mPa·s 1400 mPa·s||45 45||3.0 N/mm² 3.0 N/mm²||250 % 250 %|
|POWERSIL® 577 PLUS||- -||350000 mPa·s -||- -||- -||- -|
|POWERSIL® 590||- -||- -||- -||- -||- -|
 Tear-growth resistance | ASTM D 624 B,  动态粘度 (10 s⁻¹) | 23 °C | DIN EN ISO 3219,  动态粘度 （0.1 %形变时） | DIN 54458,  Shore density A | DIN ISO 48-4,  Breaking strength | ISO 37 type 1,  断裂伸长率 | ISO 37 type 1