VINNAPAS® EF 818
VINNAPAS® EF 818 is an aqueous dispersion of a vinyl acetate-ethylene (VAE) copolymer. It does not need a coalescing agent or plasticizer to achieve a low minimum film forming temperature. VINNAPAS® EF 818 is produced without the use of alkyl phenol ethoxylate (APEO) containing compounds. It offers a cost competitive alternative for a variety of technologies, including vinyl acrylics and styrene acrylics.
- Very good touch-up properties
- Excellent scrub resistance
- Improved alkali resistance
- Good response to associative thickeners
- Very low residual VAM (< 200 ppm)
- Allows for formulations without coalescing solvents
- Produced without the use of APEOs
As a broad application binder for architectural coatings, VINNAPAS® EF 818 provides a variety of benefits for the coatings formulator.
- It is alkylphenol ethoxylate (APEO) free meaning it does not use any surfactants or defoamers that contain APEO.
- It is manufactured without the use of any formaldehyde donors.
- It is very low in residual vinyl acetate monomer (VAM) at <0.05% and capable for end products with low content of volatile organic compounds.
- It has a low glass transition temperature (Tg) and minimum film formation temperature (MFFT) which provide the polymer with a very low to no cosolvent demand for proper film formation
VINNAPAS® EF 818 continues the standard for scrub resistance set by VAE copolymers as evidenced by evaluations of several different formulations that show it outperforming both conventional and low VOC latexes. This allows paint formulators to develop paints with extremely high levels of scrub resistance. VINNAPAS® EF 818 offers early water resistance. It can also be formulated over a broad range of PVC’s successfully replacing styrene acrylics. VINNAPAS® EF 818 exhibits excellent thickener response with a number of different thickener types, including hydrophobically modified cellulosic (HMHEC), hydrophobic ethoxylated urethanes (HEUR), and hydrophobic alkali-swellable emulsions (HASE). With the growing trend of low odor paints, it is becoming more important that the polymers used in formulations can be formulated at lower solvent levels without sacrificing performance. Many commercial binders used today, especially conventional styrene acrylics, suffer significantly in performance when formulated at lower solvent levels. VINNAPAS® EF 818 requires little to no coalescing solvent, which allows formulators to develop high performance coatings with very low odor. The reduction in solvent provided by formulating with VINNAPAS® EF 818 compared with conventional styrene acrylics can deliver additional raw material cost savings.
VINNAPAS® EF 818 represents the next in a line of VAEs that is positioned as an alternative to styrene acrylics and other technolgies in the architectural coatings industry.
Specific formulating tips are available upon request and in the future will be available in the Formulation Guidelines bulletin on the WACKER web site.
如果产品不是用于我们推荐的应用, 则购买者应对该产品的选择、加工和使用负全部责任. 此外还应遵守所有的相关法律法规.
Wacker Chemie AG
- 200 Kg Steel drum
- 220 Kg Steel drum
- 1 MT IBC
- 1.1 MT IBC
- 1 MT Returnable tote
- Flexi bag.
- Tank lorry
When the dispersion is stored in tanks, proper storage conditions must be maintained. The product has a shelf life of 9 months starting from the date of manufacture if stored in the original, unopened containers at temperatures between 5 and 30°C. Any longer periods for the maximum storage period that may be described in the Certificate of Analysis which accompanies each shipment of the product, take preference over this suggestion in which case the time period stated in the Certificate of Analysis shall be solely authoritative. Iron or galvanized-iron equipment and containers are not recommended because the dispersion is slightly acidic. Corrosion may result in discoloration of the dispersion or its blends when further processed. Therefore, the use of containers and equipment made of ceramics, rubberized or enameled materials, appropriately finished stainless steel, or plastic (e.g. rigid PVC, polyethylene or polyester resin) is recommended. As polymer dispersions may tend to superficial film formation, skins or lumps may form during storage or transportation. Filtration is therefore recommended prior to utilization of the product.
Preservation for Transport, Storage and further Processing
The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package. Measures should also be taken to ensure cleanliness of the tanks and pipes. In unstirred tanks, a layer of preservative-containing water should be sprayed onto the surface of the dispersion to prevent the formation of unwanted skin and possible attack by microorganisms. The thickness of this water layer should be < 5 mm for low viscosity dispersions and up to 10-20 mm for high viscosity products. Proper procedures - periodic tank cleaning and sanitization - must be set up in order to prevent microbial attack. Contact your biocide representative/supplier for further plant hygiene recommendations. Measures should be taken to ensure that only clean air enters the tank when the dispersion is removed. Finished products manufactured from polymer dispersions usually also require preservation. The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required. If the product is stored for a longer period, stirring is recomended before use.