VINNAPAS® EF 818

VINNAPAS® EF 818 is an aqueous dispersion of a vinyl acetate-ethylene (VAE) copolymer. It does not need a coalescing agent or plasticizer to achieve a low minimum film forming temperature. VINNAPAS® EF 818 is produced without the use of alkyl phenol ethoxylate (APEO) containing compounds. It offers a cost competitive alternative for a variety of technologies, including vinyl acrylics and styrene acrylics.



特性

  • Very good touch-up properties
  • Excellent scrub resistance
  • Improved alkali resistance
  • Good response to associative thickeners
  • Very low residual VAM (< 200 ppm)
  • Allows for formulations without coalescing solvents
  • Produced without the use of APEOs

免责声明

所提供之所有信息均基于我们当前所掌握的知识。尽管如此,我们不对其作任何担保、也不承担任何责任,并且保留在任何时候进行技术变更的权利。购买方应在预测试中对所提供之信息以及产品在既定应用中的适应性进行检查。任何时候都必须以合同条款与条件为准。此外,本免责申明还适用于与第三方权利有关之事宜,尤其是在德国境外。

Properties

As a broad application binder for architectural coatings, VINNAPAS® EF 818 provides a variety of benefits for the coatings formulator.

  • It is alkylphenol ethoxylate (APEO) free meaning it does not use any surfactants or defoamers that contain APEO.
  • It is manufactured without the use of any formaldehyde donors.
  • It is very low in residual vinyl acetate monomer (VAM) at <0.05% and capable for end products with low content of volatile organic compounds.
  • It has a low glass transition temperature (Tg) and minimum film formation temperature (MFFT) which provide the polymer with a very low to no cosolvent demand for proper film formation

VINNAPAS® EF 818 continues the standard for scrub resistance set by VAE copolymers as evidenced by evaluations of several different formulations that show it outperforming both conventional and low VOC latexes. This allows paint formulators to develop paints with extremely high levels of scrub resistance. VINNAPAS® EF 818 offers early water resistance. It can also be formulated over a broad range of PVC’s successfully replacing styrene acrylics. VINNAPAS® EF 818 exhibits excellent thickener response with a number of different thickener types, including hydrophobically modified cellulosic (HMHEC), hydrophobic ethoxylated urethanes (HEUR), and hydrophobic alkali-swellable emulsions (HASE). With the growing trend of low odor paints, it is becoming more important that the polymers used in formulations can be formulated at lower solvent levels without sacrificing performance. Many commercial binders used today, especially conventional styrene acrylics, suffer significantly in performance when formulated at lower solvent levels. VINNAPAS® EF 818 requires little to no coalescing solvent, which allows formulators to develop high performance coatings with very low odor. The reduction in solvent provided by formulating with VINNAPAS® EF 818 compared with conventional styrene acrylics can deliver additional raw material cost savings.

Application
VINNAPAS® EF 818 represents the next in a line of VAEs that is positioned as an alternative to styrene acrylics and other technolgies in the architectural coatings industry.

Processing

Specific formulating tips are available upon request and in the future will be available in the Formulation Guidelines bulletin on the WACKER web site.
 

如果 ???000012286??? 被应用于上述所提及以外的领域, 对 ???000012286??? 的选择, 处理及使用皆由购买方自行负责, 且所有行为必须依照法律法规.

有关该产品是否符合美国FDA与德国BfR所规定的食品接触要求等问题, 请联系:

Wacker Chemie AG

Hanns-Seidel-Platz 4

D-81737 Munich

Germany

储存

When the dispersion is stored in tanks, proper storage conditions must be maintained. The product has a shelf life of 9 months starting from the date of manufacture if stored in the original, unopened containers at temperatures between 5 and 30°C. Any longer periods for the maximum storage period that may be described in the Certificate of Analysis which accompanies each shipment of the product, take preference over this suggestion in which case the time period stated in the Certificate of Analysis shall be solely authoritative. Iron or galvanized-iron equipment and containers are not recommended because the dispersion is slightly acidic. Corrosion may result in discoloration of the dispersion or its blends when further processed. Therefore, the use of containers and equipment made of ceramics, rubberized or enameled materials, appropriately finished stainless steel, or plastic (e.g. rigid PVC, polyethylene or polyester resin) is recommended. As polymer dispersions may tend to superficial film formation, skins or lumps may form during storage or transportation. Filtration is therefore recommended prior to utilization of the product.

Preservation for Transport, Storage and further Processing

The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package. Measures should also be taken to ensure cleanliness of the tanks and pipes. In unstirred tanks, a layer of preservative-containing water should be sprayed onto the surface of the dispersion to prevent the formation of unwanted skin and possible attack by microorganisms. The thickness of this water layer should be < 5 mm for low viscosity dispersions and up to 10-20 mm for high viscosity products. Proper procedures - periodic tank cleaning and sanitization - must be set up in order to prevent microbial attack. Contact your biocide representative/supplier for further plant hygiene recommendations. Measures should be taken to ensure that only clean air enters the tank when the dispersion is removed. Finished products manufactured from polymer dispersions usually also require preservation. The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required.

销售和支持

Changsha Port
长沙市开福区新港大道80号
000000 Changsha
中国
+86  400  921-6699 (电话)
Contact Sales

我们可以为您提供什么帮助?

    您在选择产品方面需要帮助或者需要技术咨询? 请联系我们的专家
Ask a question

您是否需要产品样本?

您可以在此处索取产品样本。

索取样本

更多产品

产品 技术数据
玻璃化温度
专用方法
乳液薄膜外观
目测
保护性胶体/乳化剂体系 主要颗粒尺寸
专用方法
最低成膜温度
DIN ISO 2115
密度
at 20 °C
专用方法
Solids content
专用方法
pH值
DIN/ISO 976
pH值
专用方法
动力粘度
at Brookfield, spindle 1 / 20 rpm
ISO 2555
动力粘度
at 25 °C
专用方法
固体含量
DIN EN ISO 3251
PRIMIS® SAF 9000 约 21 °C 约 69.8 °F glossy glossy surface active emulsifiers surface active emulsifiers 约 70 nm 约 70 nm 约 17 °C 约 62.6 °F - - - - 6.5 - 7.5 6.5 - 7.5 - - 50 - 500 mPa·s 50 - 500 mPa·s - - 41 - 43 % 41 - 43 %
VINNAPAS® EF 818 约 7 °C 约 44.6 °F - - - - 0.19 - 0.26 µm 190E-9 - 260E-9 mil - - 大约 1.07 g/cm³ 大约 1.070 lb/gal 54.0 - 56.0 wt. % 54.0 - 56.0 wt. % - - 4.0 - 6.0 4.0 - 6.0 - - 150 - 650 mPa·s 150 - 650 mPa·s - -