VINNAPAS® DPN 16
VINNAPAS® DPN 16 is an aqueous polymer dispersion produced from vinylacetate monomer.
- Meets the requirements of strain group D3 of EN 204 without addition of a catalyst
- Low discoloration of the glue line when hot pressing
VINNAPAS® DPN 16 can be used as raw material for water resistant wood glues.
如果产品不是用于我们推荐的应用, 则购买者应对该产品的选择、加工和使用负全部责任. 此外还应遵守所有的相关法律法规.
Wacker Chemie AG
When the dispersion is stored in tanks, proper storage conditions must be maintained. The product has a shelf life of 6 months starting from the date of receipt if stored in the original, unopened containers at temperatures between 5 and 30 °C. Any longer periods for the maximum storage period that may be described in the Certificate of Analysis which accompanies each shipment of the product, take preference over this suggestion in which case the time period stated in the Certificate of Analysis shall be solely authoritative. Iron or galvanized iron containers and equipment are not recommended. Corrosion could result in discoloration of the dispersion or blends made from it in further processing. We therefore recommend the use of containers and equipment made of ceramic, rubberized or enameled materials, appropriately finished stainless steel, or plastic (rigid PVC, polyethylene or polyester resin). As polymer dispersions may tend to superficial film formation, skins or lumps may be formed during storage or transportation. A filtration process is thus recommended prior to utilization of the product.
Preservation for Transport, Storage and further Processing
The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package.
Measures should also be taken to ensure cleanliness of the tanks and pipes. In unstirred tanks, a layer of preservative-containing water should be sprayed onto the surface of the dispersion to prevent the formation of unwanted skin and possible attack by microorganisms. The thickness of this water layer should be < 5 mm for low viscosity dispersions and up to 10–20 mm for high viscosity products. Proper procedures – periodic tank cleaning and sanitization – must be set up in order to prevent microbial attack. Contact your biocide representative/supplier for further plant hygiene recommendations. Measures should be taken to ensure that only clean air enters the tank when the dispersion is removed.
Finished products manufactured from polymer dispersions usually also require preservation. The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required.
|VINNAPAS® DPN 15||2.5 - 3.5 2.5 - 3.5||matt matt||聚乙烯醇 聚乙烯醇||12000 - 18000 mPa·s 12000 - 18000 mPa·s||51 - 53 % 51 - 53 %||tack free tack free||can be thawed after being frozen once to -10°C can be thawed after being frozen once to -10°C||5 °C 41.0 °F||约 28 °C 约 82.4 °F|
|VINNAPAS® DPN 16||2.5 - 3.5 2.5 - 3.5||matt matt||聚乙烯醇 聚乙烯醇||10000 - 14000 mPa·s 10000 - 14000 mPa·s||50 - 54 % 50 - 54 %||tack free tack free||can be thawed after being frozen once to -10°C can be thawed after being frozen once to -10°C||5 °C 41.0 °F||约 28 °C 约 82.4 °F|
|VINNAPAS® DPX 271||5 - 7 5 - 7||matt matt||聚乙烯醇 聚乙烯醇||6000 - 14000 mPa·s 6000 - 14000 mPa·s||44 - 48 % 44 - 48 %||tack free tack free||protect from freezing protect from freezing||5 °C 41.0 °F||约 30 °C 约 86.0 °F|
 最低成膜温度 | DIN ISO 2115,  抗冻性 | 专用方法,  乳液薄膜外观 | 目测,  玻璃化温度 | 专用方法