VINNAPAS® EZ 222

VINNAPAS® EZ 222 is a hydroxyethyl cellulose/surfactant stabilized vinyl acetate-ethylene (VAE) copolymer dispersion with a glass transition temperature (Tg) of +18.0°C.



特性

  • Excellent scrub resistance
  • Good flow and leveling
  • Low viscosity 
  • High solids content 
  • Produced without the use of APEOs

免责声明

所提供之所有信息均基于我们当前所掌握的知识。尽管如此,我们不对其作任何担保、也不承担任何责任,并且保留在任何时候进行技术变更的权利。购买方应在预测试中对所提供之信息以及产品在既定应用中的适应性进行检查。任何时候都必须以合同条款与条件为准。此外,本免责申明还适用于与第三方权利有关之事宜,尤其是在德国境外。

Protect against frost.

VINNAPAS® EZ 222 can be used in flat to mid-sheen DIY architectural coatings applications. It provides excellent scrub resistance and the large particle size provides good flow and leveling. Furthermore, the dispersion can be used in intumescent coatings formulations.

VINNAPAS® EZ 222 is manufactured without the use of any surfactants or defoamers that contain alkylphenol ethoxylates.

VINNAPAS® EZ 222 can be thickened using such materials as hydroxyethyl cellulose or polyacrylic acid-acrylamide copolymer resins. VINNAPAS® EZ 222 will accept high loadings of such fillers as calcium carbonate and clay without appreciably changing the viscosity.

储存

When the dispersion is stored in tanks, proper storage conditions must be maintained. If stored in the original, unopened containers at cool (below 30 °C), but frost-free temperatures the product has a shelf life of 9 months from the date of manufacture. Any longer periods for the maximum storage period that may be described in the Certificate of Analysis which accompanies each shipment of the product, take preference over this suggestion in which case the time period stated in the Certificate of Analysis shall be solely authoritative. Iron or galvanized-iron equipment and containers are not recommended because the dispersion is slightly acidic. Corrosion may result in discoloration of the dispersion or its blends when further processed. Therefore, the use of containers and equipment made of ceramics, rubberized or enameled materials, appropriately finished stainless steel, or plastic (e.g. rigid PVC, polyethylene or polyester resin) is recommended. As polymer dispersions may tend to superficial film formation, skins or lumps may form during storage or transportation. Filtration is therefore recommended prior to utilization of the product.

Preservation for Transport, Storage and further Processing

The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package. To maintain proper storage conditions appropriate measures should also be taken to ensure cleanliness of the tanks and pipes. In a storage tank in which the product is not stirred, it is advisable to contact your biocide representative/supplier. Proper procedures must be set up in order to prevent microbial attack between necessary periodic tank cleaning and sanitization. These procedures will vary, since loading and unloading practices in each storage situation will differ slightly. Finished products manufactured from polymer dispersions usually also require preservation. The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required.

 

Additional information

If VINNAPAS® EZ 222 is used in applications other than those mentioned, the choice, processing and use of VINNAPAS® EZ 222 is the sole responsibility of the purchaser. All legal and other regulations must be complied with.

销售和支持

Changsha Port
长沙市开福区新港大道80号
000000 Changsha
中国
+86  400  921-6699 (电话)
Contact Sales

我们可以为您提供什么帮助?

    您在选择产品方面需要帮助或者需要技术咨询? 请联系我们的专家
Ask a question

您是否需要产品样本?

您可以在此处索取产品样本。

索取样本

更多产品

产品 技术数据
玻璃化温度
专用方法
成膜表面
专用方法
乳液薄膜外观
目测
与颜料和填料的相容性
专用方法
保护性胶体/乳化剂体系 保护性胶体/乳化剂体系 主要颗粒尺寸
专用方法
抗冻性
专用方法
最低成膜温度
DIN ISO 2115
密度
DIN EN ISO 2811-1
密度
at 20 °C
专用方法
密度
at 20 °C
ISO 2811
Solids content
DIN EN ISO 3251
Solids content
专用方法
pH值
DIN/ISO 976
pH值
专用方法
动力粘度
at 23 °C
ISO 2555
动力粘度
at 25 °C
专用方法
固体含量
DIN EN ISO 3251
PRIMIS® KT 3000 - - - - - - very good very good - - - - - - protect from freezing protect from freezing - - 大约 1 g/cm³ 大约 1.000 lb/gal - - - - 15 - 19 wt. % 15 - 19 wt. % - - 13 13 - - 50 - 110 mPa·s 50 - 110 mPa·s - - - -
PRIMIS® SAF 9000 约 21 °C 约 69.8 °F - - glossy glossy - - surface active emulsifiers surface active emulsifiers - - 约 70 nm 约 70 nm - - 约 17 °C 约 62.6 °F - - - - - - - - - - 6.5 - 7.5 6.5 - 7.5 - - 50 - 500 mPa·s 50 - 500 mPa·s - - 41 - 43 % 41 - 43 %
VINNAPAS® EF 818 约 7 °C 约 44.6 °F - - - - - - - - - - 0.19 - 0.26 µm 190E-9 - 260E-9 mil - - - - - - 大约 1.07 g/cm³ 大约 1.070 lb/gal - - - - 54.0 - 56.0 wt. % 54.0 - 56.0 wt. % - - 4.0 - 6.0 4.0 - 6.0 - - 150 - 650 mPa·s 150 - 650 mPa·s - -
VINNAPAS® EP 3036 NJG 约 0 - 4 °C 约 32.0 - 39.2 °F slight dry tack slight dry tack clear glossy clear glossy very good very good - - 聚乙烯醇 聚乙烯醇 - - protect from freezing protect from freezing 约 0 °C 约 32.0 °F - - - - 大约 1.07 g/cm³ 大约 1.070 lb/gal - - - - 4.0 - 6.0 4.0 - 6.0 - - 4400 - 5400 mPa·s 4400 - 5400 mPa·s - - > 54.5 % > 54.5 %