WACKER® CATALYST T 77 PLUS
WACKER® CATALYST T 77 PLUS is a standard curing agent for condensation curing RTV-2 silicones. When processed with a base compound of the product series ELASTOSIL® RT or ELASTOSIL® M, a durable and self bonding silicone rubber is formed after curing.
特性
- Non-slump paste
- To be processed with base compounds of the ELASTOSIL® RT or ELASTOSIL® M series (recommended mixing ratio: 10:1)
- Very fast curing at room temperature
- Curing speed tunable by mixing ratio
- Provides condensation curing RTV-2 silicones with excellent adhesion to many substrates (glass, ceramics, wood, metals, plastics and powder coatings)
WACKER® CATALYST T 77 PLUS的特殊性能
- 剪切变稀
- 缩合固化
- 自粘性
- 触变
- General purpose curing agent for condensation curing RTV-2 silicone rubber bases
- Typical fields of application: household appliances, automotive, mechanical engineering, electrical industry.
WACKER® CATALYST T 77 PLUS is used as standard curing agent for ELASTOSIL® RTV-2 base compounds. The shear-thinning paste provides any product of the series ELASTOSIL® RT or ELASTOSIL® M with excellent adhesion properties. The adhesion strength of the cured rubber usually is independent of the type of base compound used. A general overview in regard to adhesion quality is given in adjacent table.
The crosslinking reaction of condensation curing RTV-2 silicones is relatively robust in regard to curing inhibition. Amine containing materials, urethanes, organic compounds with sulfur-containing groups, organometallic compounds, plasticizers, lubricants, oils and grease usually do not impair the curing process itself. Nevertheless, for optimum adhesion results all substrates used should be clean, dry and free from grease, waxes, dust or other surface contaminations.
Mixing and curing:
To ensure uniform curing both components (rubber base and curing agent) have to be thoroughly mixed, either manually or by automatic metering lines equipped with static or dynamic mixing devices. The recommended mixing ratio is 10:1 by weight.
Potlife and curing speed can be modified within limits by adjusting the ratio of base compound to curing agent. Varying the mixing ratio between 8:1 and 12:1 usually has a small effect on the properties of the cured rubber. However, if the mixing ratio differs substantially from the recommended scope, preliminary tests should be carried out to check the cured material’s suitability. General information about pot life and resulting curing times is given in the respective tables "Catalyzed".
Moreover curing speed can be slightly accelerated by raising the temperature. Heating, however, must not exceed 60 °C before curing is completed.
After completion of the vulcanization process the self-bonding silicone rubber may continuously be exposed to constantly changing climatic conditions, UV radiation and high temperature without damage. For further details regarding specific silicone properties consult the technical datasheet of the respective RTV-2 base compound.
Removal:
If removal of silicone rubber from machines or dispensing equipment is necessary, white spirit or similar nonpolar solvents are recommended. However, cleaning ideally should take place before the silicone is fully vulcanized. Cured silicone rubber needs to be removed mechanically, if necessary in combination with a swelling agent (solvent).
Detailed information about processing RTV-2 silicones is given in our brochure “ROOM TEMPERATURE VULCANIZING (RTV) SILICONES - MATERIAL AND PROCESSING GUIDELINES”. We recommend running preliminary tests to optimize conditions for the particular application.
储存
Store in a dry and cool place.
The 'Best use before end' date of each batch is shown on the product label.
Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.