ELASTOSIL® SUB C 2002 A/B
ELASTOSIL® Sub C 2002 A/B is a low viscous, free flowing two-component, addition-curing silicone rubber specially designed for deepsea applications.
- Two-part systen, 10:1 mixing ratio
- low viscous, free flowing
- fast and non-shrink cure at room temperature
- thermal acceleration with moderate temperature
- excellent long-term stability of the mechanical properties of the vulcanizate
- translucent, pigmentable in any color
ELASTOSIL® SUB C 2002 A/B的特殊性能
- 具体特征: 优异的储存稳定性
- 具体特征: 低粘度
- 具体特征: 快速固化
- 具体特征: 高抗撕裂性能
- 流变性: 低粘度
- 硫化胶: 可在最低-40°C和最高+180°C下保持柔韧性
- 耐久性: 可在最低-40°C和最高+180°C下保持柔韧性
ELASTOSIL® Sub C 2002 A/B is the silicone rubber of choice to manufacture all types of thermal insulating devices
Main field of application: Thermal insulation material for marine applications, e.g. deep-sea constructions and subsea oil
Only A and B components with the same batch number may be processed together!
- Surface preparation
All surfaces must be clean and free of contaminants that will inhibit the cure of ELASTOSIL® Sub C 2002 A/B. Examples of inhibiting contaminants are sulfur containing materials, plasticizers, urethanes, amine containing materials and organometallic compounds – especially organotin compounds. If a substrate’s ability to inhibit cure is unknown, a small scale test should be run to determine compatibility.
Component A of ELASTOSIL® Sub C 2002 A/B contains the platinum catalyst, component B the crosslinker. Even traces of the platinum catalyst may cause gelling of the component containing the crosslinker. Therefore tools (spatula, stirrers, etc.) used for handling the platinum-containing component or the catalyzed compound must not come into contact with this component. The two components should be thoroughly mixed at a 10 : 1 ratio by weight or volume.
To eliminate any air eventually introduced during mixing, the A/B mix can be deaerated under vacuum prior use (25 - 50 mbar, 10 - 15 min). For processing ELASTOSIL® Sub C 2002 A/B in industrial scale, the use of automatic mixing and dispensing equipment is recommended.
The curing time of addition-curing silicone rubber is highly dependent on temperature, size and heat sink properties of the components being potted or bonded.
The reactivity can be adjusted within wide limits by adding Catalyst EP or Inhibitor PT 88 to suit the processing requirements of the particular application. Catalyst EP increases the reactivity, i.e. pot life and curing time are reduced. Inhibitor PT 88 is a pot life extender and prolongs pot life and curing time. Further information is given in our leaflet “Catalyst EP/Inhibitor PT88”.
After completion of the vulcanization process the product may be exposed continuously and without damage to marine or subsea conditions, UV radiation, temperature levels as high as 150 °C (302 °F) and isostatic water pressure of up to 200 bar.
We recommend running preliminary tests to optimize conditions for the particular application. Comprehensive processing instructions are given in our leaflet "Processing RTV-2 Silicone Rubber". Bonding To achieve a good bonding of ELASTOSIL® Sub C 2002 A/B to sector-specific substrates, it is recommended to use a primer of the WACKER® Primer G series.
If removal of silicone rubber from machines or dispensing equipment is necessary, white spirit or similar non-polar solvents are recommended. However, cleaning ideally should take place before the rubber is fully vulcanized. Cured silicone rubber can be removed by mechanical means, preferably in combination with a swelling agent (solvent).
Detailed processing instructions are given in our brochure “ROOM TEMPERATURE VULCANIZING (RTV) SILICONES - MATERIAL AND PROCESSING GUIDELINES
The 'Best use before end' date of each batch is shown on the product label.
Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.
|动态粘度||Tear-growth resistance||Shore density A||Breaking strength||断裂伸长率|
|ELASTOSIL® SUB C 2002 A/B||950 mPa·s 950 mPa·s||18 N/mm 18 N/mm||42 42||5.1 N/mm² 5.1 N/mm²||300 % 300 %|
 动态粘度 D = 0.5 1/s | ISO 3219,  Tear-growth resistance | based on ASTM D 624 B / 23°C / t = 2 mm,  Shore density A | DIN ISO 48-4,  Breaking strength | ISO 37 Type 1 / 23°C / t = 2 mm,  断裂伸长率 | ISO 37 Type 1 / 23°C / t = 2 mm