ELASTOSIL® M 4512

$ELASTOSIL<sup>®</sup> M 4512

Pourable, condensation-curing, two-component silicone rubber that vulcanizes at room temperature.

 

Main application: Making cost effective molds, especially suited for casting PE and PU resins.



特性

  • very good flowability and self-deaeration
  • low Shore A hardness (approx. 20)
  • excellent tear strength
  • very high elongation and flexibility
  • outstanding chemical resistance to attack by polyester and polyurethane resins, mold life is significantly extended

ELASTOSIL® M 4512的特殊性能

  • 双组分
  • 缩合固化

免责声明

所提供之所有信息均基于我们当前所掌握的知识。尽管如此,我们不对其作任何担保、也不承担任何责任,并且保留在任何时候进行技术变更的权利。购买方应在预测试中对所提供之信息以及产品在既定应用中的适应性进行检查。任何时候都必须以合同条款与条件为准。此外,本免责申明还适用于与第三方权利有关之事宜,尤其是在德国境外。

ELASTOSIL® M 4512 is a high-performance moldmaking compound, which is particularly suitable for the reproduction of models with extensive undercuts.

ELASTOSIL® M 4512 is especially suitable for the processing of polyester and polyurethane resins.

If molds for processing epoxy or polyurethane resins are to be made,ELASTOSIL® M 4512 is cured by adding 5 wt % Catalyst T 21.


For molds used to process other reproduction materials such as polyester resins, plaster, concrete, synthetic stone, wax or low-melting alloys, 5 wt % Catalyst T 51 should be used.


Pot lifes and curing times of both catalysts may be accelerated, and thus adjusted to suit the individual application by blending with Catalyst T 47.
For faster curing either catalyst may be blended with Catalyst T 47. E.g. at a ratio of 95 : 5 (T51 : T47) the pot life decreases to about 30 min, and the mold needs only about 4 h to cure.
Further instructions on blending any catalyst with Catalyst T 47 may be found in our data-sheet: "WACKER® T-series catalysts".

The pot life is the period of time at 23 °C / 50 % rel. humidity during which the catalyzed mix to attain a viscosity of 100,000 mPa s and still be just pourable

 

Please check also our brochures and info sheets.

 


 

储存

The 'Best use before end' date of each batch is shown on the product label.

Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

销售和支持

Wacker Chemicals (China) Co.,Ltd.
Caohejing Hi-Tech Park
200233 Shanghai
中国大陆
+86  21  6130-2000 (电话)
+86 21 6130-2500  (传真)
Contact Sales

我们可以为您提供什么帮助?

  • 您在选择产品方面需要帮助或者需要技术咨询? 请联系我们的专家
Ask a question

您是否需要产品样本?

您可以在此处索取产品样本。

索取样本

更多产品

产品 技术数据
动态粘度 Tear-growth resistance Dropping period Shore density A Breaking strength 断裂伸长率
CENUSIL® M 810 A/B 3000 mPa·s[1] 3000 mPa·s[1] 15 N/mm[13] 15 N/mm[13] - - 10[15] 10[15] 3.5 N/mm²[18] 3.5 N/mm²[18] 600 %[20] 600 %[20]
CENUSIL® M 820 A/B 6000 mPa·s[2] 6000 mPa·s[2] - - - - 20[15] 20[15] 4 N/mm²[18] 4 N/mm²[18] 500 %[20] 500 %[20]
CENUSIL® M 825 A/B 8000 mPa·s[3] 8000 mPa·s[3] 20 N/mm[13] 20 N/mm[13] - - 25[15] 25[15] 5 N/mm²[18] 5 N/mm²[18] 450 %[20] 450 %[20]
CENUSIL® M 830 A/B 8000 mPa·s[3] 8000 mPa·s[3] > 20 N/mm[13] > 20 N/mm[13] - - 26[15] 26[15] 5 N/mm²[18] 5 N/mm²[18] 500 %[20] 500 %[20]
ELASTOSIL® M 1470 - - > 10 N/mm[13] > 10 N/mm[13] - - 45[15] 45[15] 4.5 N/mm²[18] 4.5 N/mm²[18] 230 %[20] 230 %[20]
ELASTOSIL® M 4115 A/B 2500 mPa·s[3] 2500 mPa·s[3] 5 N/mm[13] 5 N/mm[13] - - 17[15] 17[15] 3 N/mm²[18] 3 N/mm²[18] 400 %[20] 400 %[20]
ELASTOSIL® M 4119 A/B 3000 mPa·s[1] 3000 mPa·s[1] - - - - 20 20 3.5 N/mm²[18] 3.5 N/mm²[18] > 400 %[20] > 400 %[20]
ELASTOSIL® M 4125 F A/B 6000 mPa·s[3] 6000 mPa·s[3] - - - - 28[15] 28[15] 5.0[19] 5.0[19] 500[20] 500[20]
ELASTOSIL® M 4370 A/B 350 mPa·s[4] 350 mPa·s[4] > 4 N/mm[13] > 4 N/mm[13] - - 55[16] 55[16] 3.0 N/mm²[18] 3.0 N/mm²[18] 130 %[20] 130 %[20]
ELASTOSIL® M 4400 30000 mPa·s[5] 30000 mPa·s[5] > 3 N/mm[13] > 3 N/mm[13] - - 23[15] 23[15] 2 N/mm²[18] 2 N/mm²[18] 250 %[20] 250 %[20]
ELASTOSIL® M 4440 25000 mPa·s[5] 25000 mPa·s[5] 4.5 N/mm[13] 4.5 N/mm[13] - - 37[15] 37[15] 2.5 N/mm²[18] 2.5 N/mm²[18] 220 %[20] 220 %[20]
ELASTOSIL® M 4470 15000 mPa·s[6] 15000 mPa·s[6] > 4 N/mm[13] > 4 N/mm[13] - - 60[15] 60[15] 4.5 N/mm²[18] 4.5 N/mm²[18] 120 %[20] 120 %[20]
ELASTOSIL® M 4503 40000 mPa·s[7] 40000 mPa·s[7] > 20 N/mm[13] > 20 N/mm[13] - - 25[16] 25[16] - 350 %[20] 350 %[20]
ELASTOSIL® M 4511 25000 mPa·s[5] 25000 mPa·s[5] > 18 N/mm[13] > 18 N/mm[13] - - 12[15] 12[15] 3.5 N/mm²[18] 3.5 N/mm²[18] 600 %[20] 600 %[20]
ELASTOSIL® M 4512 30000 mPa·s[5] 30000 mPa·s[5] > 24 N/mm[13] > 24 N/mm[13] - - 20[15] 20[15] 3.5 N/mm²[18] 3.5 N/mm²[18] 500 %[20] 500 %[20]
ELASTOSIL® M 4514 35000 mPa·s[8] 35000 mPa·s[8] > 25 N/mm[13] > 25 N/mm[13] - - 25[16] 25[16] 4.5 N/mm²[18] 4.5 N/mm²[18] 450 %[20] 450 %[20]
ELASTOSIL® M 4541 40000 mPa·s[6] 40000 mPa·s[6] > 30 N/mm[13] > 30 N/mm[13] - - 32[15] 32[15] 5 N/mm²[18] 5 N/mm²[18] 400 %[20] 400 %[20]
ELASTOSIL® M 4600 A/B 20000 mPa·s[6] 20000 mPa·s[6] > 20 N/mm[13] > 20 N/mm[13] 90 min 90 min 20[15] 20[15] 7[18] 7[18] 800 %[20] 800 %[20]
ELASTOSIL® M 4601 A/B 15000 mPa·s[9] 15000 mPa·s[9] > 30 N/mm[13] > 30 N/mm[13] - - 28[15] 28[15] 6.5 N/mm²[18] 6.5 N/mm²[18] 700 %[20] 700 %[20]
ELASTOSIL® M 4642 A/B 20000 mPa·s[9] 20000 mPa·s[9] > 30 N/mm[13] > 30 N/mm[13] - - 37[15] 37[15] 7 N/mm²[18] 7 N/mm²[18] 480 %[20] 480 %[20]
ELASTOSIL® M 4643 A/B 40000 mPa·s[6] 40000 mPa·s[6] > 10 N/mm[13] > 10 N/mm[13] - - 48[15] 48[15] 5 N/mm²[18] 5 N/mm²[18] 300 %[20] 300 %[20]
ELASTOSIL® M 4670 A/B 120000 mPa·s[9] 120000 mPa·s[9] > 12 N/mm[13] > 12 N/mm[13] - - 55[15] 55[15] 5.5 N/mm²[18] 5.5 N/mm²[18] 250 %[20] 250 %[20]
ELASTOSIL® RT 480 300000 - 400000 mPa·s[10] 300000 - 400000 mPa·s[10] > 7 N/mm[13] > 7 N/mm[13] - - 55[15] 55[15] 4.5 N/mm²[18] 4.5 N/mm²[18] 170 %[20] 170 %[20]
ELASTOSIL® RT 625 A/B 25000 mPa·s[6] 25000 mPa·s[6] 30 N/mm[13] 30 N/mm[13] - - 25[15] 25[15] 6.5 N/mm²[18] 6.5 N/mm²[18] 600 %[20] 600 %[20]
ELASTOSIL® RT 646 A/B 110000 mPa·s[3] 110000 mPa·s[3] 12 N/mm[13] 12 N/mm[13] - - 53[17] 53[17] 5 N/mm²[18] 5 N/mm²[18] 280 %[20] 280 %[20]
ELASTOSIL® RT K - - > 3 N/mm[14] > 3 N/mm[14] - - 45[15] 45[15] 2 N/mm²[18] 2 N/mm²[18] 130 %[20] 130 %[20]
ELASTOSIL® VARIO 15 5.000 mPa·s[11] 5.000 mPa·s[11] 15[13] 15[13] - - 15[15] 15[15] 6.5 N/mm²[18] 6.5 N/mm²[18] 900 %[20] 900 %[20]
ELASTOSIL® VARIO 40 15.000 mPa·s[12] 15.000 mPa·s[12] 15 N/mm[13] 15 N/mm[13] - - 40[15] 40[15] 8[18] 8[18] 450 %[20] 450 %[20]
说明
[1] 动态粘度 | Brookfield,  [2] 动态粘度 23°C | ISO 3219,  [3] 动态粘度 | 23 °C | ISO 3219,  [4] 动态粘度 搅拌后 | 23 °C ,  [5] 动态粘度 after stirring | 23 °C | DIN EN ISO 3219,  [6] 动态粘度 after stirring | 23 °C | ISO 3219,  [7] 动态粘度 after stirring | 23.0 °C | ISO 3219,  [8] 动态粘度 (after stirring) | 23 °C | ISO 3219,  [9] 动态粘度 搅拌后 | 23 °C | ISO 3219,  [10] 动态粘度 | 23 °C | Brookfield,  [11] 动态粘度 23°C, stirred | ISO 3219,  [12] 动态粘度 23° C, stirred | ISO 3219,  [13] Tear-growth resistance | ASTM D 624 B,  [14] Tear-growth resistance | ASTM 624 B,  [15] Shore density A | ISO 868,  [16] Shore density A | DIN ISO 48-4,  [17] Shore density A | DIN 53505 / ISO 868,  [18] Breaking strength | ISO 37,  [19] Breaking strength | DIN ISO 37,  [20] 断裂伸长率 | ISO 37 