ELASTOSIL® M 4503
Pourable, condensation-curing, two-component silicone rubber that vulcanizes at room temperature.
Main application: Making cost effective molds, particularly for casting PE resins.
- Good flow
- Low Shore A hardness (approx. 25)
- Great extensibility and elasticity
- High resistance to casting resins, particularly polyesters
ELASTOSIL® M 4503的特殊性能
Due to its good mechanical properties of the cured material as well as its high resistance to polyester resins, ELASTOSIL® M 4503 is particularly suitable as a mold-making material for reproducing models with very pronounced undercuts in polyester resins.
Other materials, such as plaster or wax, may also be cast without any problems from molds made of ELASTOSIL® M 4503.
ELASTOSIL® M 4503 is cured by adding 5 wt % Catalyst T35 Pot life curing time may be accelerated, and thus adjusted to suit the individual application by blending with Catalyst T47.
The pot life is the period of time at 23 °C / 50% rel. humidity during which the catalyzed mix to attain a viscosity of 100000 mPa s and still be just pourable.
For faster curing Catalyst T 35 may be blended with Catalyst T 47. E.g. at a ratio of 95 : 5 (T35 : T47) the pot life decreases to about 30 min, and the mold needs only about 4 h to cure.
Further instructions on blending any catalyst with Catalyst T 47 may be found in our data-sheet: "WACKER® T-series catalysts".
Comprehensive instructions are given in our leaflet "ELASTOSIL® - PROCESSING RTV-2 SILICONE RUBBERS".
Detailed information on other mold-making compounds in the ELASTOSIL ® M range is contained in our brochure “ELASTOSIL® M. Silicone Rubber for Mold Making”.