VINNAPAS® EP 705A (ULS)
VINNAPAS® EP 705A (ULS) is a vinyl acetate-ethylene copolymer developed as a base polymer for high-performance adhesives also produced without the use of formaldehyde donors. The low product viscosity as well as good Newtonian flow behavior of VINNAPAS® EP 705A (ULS) is good for high-speed packaging machines.
- VINNAPAS® EP 705A (ULS) is chemically stable at both high and low pH.
- It is compatible with other polyvinyl acetate (PVAc) polymers, rubber lattices, EVCL dispersions and VINNAPAS® VAE dispersions.
- It is also compatible with an assortment of resins, solvents, plasticizers and other modifiers.
VINNAPAS® EP 705A (ULS) forms strong bonds between porous substrates and various films. VINNAPAS® EP 705A (ULS) bonds such widely diversified substrates as paper, wood, cotton cloth, nylon cloth, hardboard, urethane foam and certain types of coated paperboard.
Typical application fields of VINNAPAS® EP 705A (ULS) are as follows:
- Packaging (window cartons and carton forming)
- Luggage and handbags
- Envelop and bookbinding
- Textiles or upholstery
It has a good stability at high-speed machines and is suitable for either of roll, extruder or spray application.
如果产品不是用于我们推荐的应用, 则购买者应对该产品的选择、加工和使用负全部责任. 此外还应遵守所有的相关法律法规.
Wacker Chemie AG
- 200 Kg Steel drum
- 220 Kg Steel drum
- 1 MT IBC
- 1.1 MT IBC
- 1 MT Returnable tote
- Flexi bag.
- Tank lorry
When the dispersion is stored in tanks, proper storage conditions must be maintained. The product has a shelf life of 9 months starting from the date of manufacture if stored in the original, unopened containers at temperatures between 5 and 30°C. Any longer periods for the maximum storage period that may be described in the Certificate of Analysis which accompanies each shipment of the product, take preference over this suggestion in which case the time period stated in the Certificate of Analysis shall be solely authoritative. Iron or galvanized-iron equipment and containers are not recommended because the dispersion is slightly acidic. Corrosion may result in discoloration of the dispersion or its blends when further processed. Therefore, the use of containers and equipment made of ceramics, rubberized or enameled materials, appropriately finished stainless steel, or plastic (e.g. rigid PVC, polyethylene or polyester resin) is recommended. As polymer dispersions may tend to superficial film formation, skins or lumps may form during storage or transportation. Filtration is therefore recommended prior to utilization of the product.
Preservation for Transport, Storage and further Processing
The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package. Measures should also be taken to ensure cleanliness of the tanks and pipes. In unstirred tanks, a layer of preservative-containing water should be sprayed onto the surface of the dispersion to prevent the formation of unwanted skin and possible attack by microorganisms. The thickness of this water layer should be < 5 mm for low viscosity dispersions and up to 10-20 mm for high viscosity products. Proper procedures - periodic tank cleaning and sanitization - must be set up in order to prevent microbial attack. Contact your biocide representative/supplier for further plant hygiene recommendations. Measures should be taken to ensure that only clean air enters the tank when the dispersion is removed. Finished products manufactured from polymer dispersions usually also require preservation. The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required. If the product is stored for a longer period, stirring is recomended before use.