VINNAPAS® EF 8300
- High block resistance
- High wet adhesion/water resistance
- Excellent stain resistance
- Maintains good scrub resistance
- Very low residual VAM (< 200 ppm)
- Allows formulation without coalescing solvents
- Produced without the use of APEOs
Comprehensive instructions are given in the corresponding Material Safety Data Sheets. They are available on request from WACKER subsidiaries or may be downloaded via WACKER web site http://www.wacker.com.
As a broad application, high performance binder for architectural coatings, VINNAPAS® EF 8300 was designed to combine excellent performance properties (including good block resistance, scrub resistance, and wet adhesion) with the ability to formulate low VOC paints. With the ever-tightening restrictions on the permissible level of VOCs in coatings, it is becoming more important that the polymers used can be formulated at lower solvent levels without sacrificing performance.
Many commercial binders used today, especially conventional vinyl acrylics and pure acrylics, suffer significantly in performance when formulated at lower solvent levels. VINNAPAS® EF 8300 requires little to no coalescing solvent, which allows formulators to develop high performance coatings even in low VOC paints. Therefore, it is in compliance with any major foreseeable requirements in the coatings industry.
Recommended applications include:
- Multiple interior applications, from wall paint to trim paint
- Flat finishes through to high gloss paints; particularly recommended for satin and semi-gloss paints
- Suitable for both contractor and DIY applications
VINNAPAS® EF 8300 is positioned as an alternative to other technologies such as vinyl acrylics, acrylics, and blend systems in interior architectural applications. VINNAPAS® EF 8300 is also very compatible with other latex dispersions and can be blended with other polymers such as high Tg pure acrylics to provide excellent block resistance and wet adhesion–properties that are necessary in very high end coatings.
Specific formulating tips are available upon request and in the future will be available in the Formulation Guidelines bulletin on the WACKER web site.
如果产品不是用于我们推荐的应用, 则购买者应对该产品的选择、加工和使用负全部责任. 此外还应遵守所有的相关法律法规.
Wacker Chemie AG
When the dispersion is stored in tanks, proper storage conditions must be maintained. If stored in the original, unopened containers at cool (below 30 °C), but frost-free temperatures the product has a shelf life of 9 months from the date of manufacture. Any longer periods for the maximum storage period that may be described in the Certificate of Analysis which accompanies each shipment of the product, take preference over this suggestion in which case the time period stated in the Certificate of Analysis shall be solely authoritative. Iron or galvanized-iron equipment and containers are not recommended because the dispersion is slightly acidic. Corrosion may result in discoloration of the dispersion or its blends when further processed. Therefore, the use of containers and equipment made of ceramics, rubberized or enameled materials, appropriately finished stainless steel, or plastic (e.g. rigid PVC, polyethylene or polyester resin) is recommended. As polymer dispersions may tend to superficial film formation, skins or lumps may form during storage or transportation. Filtration is therefore recommended prior to utilization of the product.
Preservation for Transport, Storage and further Processing
The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package. To maintain proper storage conditions appropriate measures should also be taken to ensure cleanliness of the tanks and pipes. In a storage tank in which the product is not stirred, it is advisable to contact your biocide representative/supplier. Proper procedures must be set up in order to prevent microbial attack between necessary periodic tank cleaning and sanitization. These procedures will vary, since loading and unloading practices in each storage situation will differ slightly. Finished products manufactured from polymer dispersions usually also require preservation. The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required.
|VINNAPAS® EF 818||- -||150 - 650 mPa·s 150 - 650 mPa·s||大约 1.07 g/cm³ 大约 8.93 lb/gal||- -||- -||约 7 °C 约 44.6 °F|
|VINNECO® CT 7030||47 - 49 % 47 - 49 %||800 - 2800 mPa·s 800 - 2800 mPa·s||大约 1.07 g/cm³ 大约 1,070 lb/gal||ionic and nonionic surfactants ionic and nonionic surfactants||very good very good||- -|
|VINNECO® EF 3777 (100 MB)||55 - 57 % 55 - 57 %||150 - 1850 mPa·s 150 - 1850 mPa·s||大约 1.07 g/cm³ 大约 1,070 lb/gal||surface active emulsifiers surface active emulsifiers||very good very good||- -|
|VINNECO® EF 3777 (60 MB)||55 - 57 % 55 - 57 %||150 - 1850 mPa·s 150 - 1850 mPa·s||大约 1.07 g/cm³ 大约 1,070 lb/gal||surface active emulsifiers surface active emulsifiers||very good very good||- -|
|VINNECO® EP 3360 (100 MB)||59 - 61 % 59 - 61 %||3000 - 6000 mPa·s 3000 - 6000 mPa·s||大约 1.07 g/cm³ 大约 1,070 lb/gal||离子型和非离子型表 面活性剂及聚合物类 化合物 离子型和非离子型表 面活性剂及聚合物类 化合物||very good very good||约 10 °C 约 50.0 °F|
|VINNECO® EP 3360 (60 MB)||59 - 61 % 59 - 61 %||3000 - 6000 mPa·s 3000 - 6000 mPa·s||大约 1.07 g/cm³ 大约 1,070 lb/gal||离子型和非离子型表 面活性剂及聚合物类 化合物 离子型和非离子型表 面活性剂及聚合物类 化合物||very good very good||约 10 °C 约 50.0 °F|
 玻璃化温度 | 专用方法,  保护性胶体/乳化剂体系 | 专用方法,  与颜料和填料的相容性 | 专用方法