VINNAPAS® eco 192

$VINNAPAS<sup>®</sup> eco 192

VINNAPAS® eco 192  is a self-crosslinking, aqueous polymer dispersion produced from the monomers vinyl acetate and ethylene for the Nonwovens market. The dispersion is produced without the use of plasticizers.

VINNAPAS® eco 192  is a fossil resources saving product. With the purchase of this product, 100 % of the fossil-based raw materials required for manufacturing of this product are replaced by sustainably certified biomass. The Substitution is based on the REDcert² biomass balance approach audited by TÜV Nord.



特性

  • VINNAPAS® eco 192 offers a unique balance of high dry and wet strength, excellent absorbent properties, and imparts good handfeel.
  • The dispersion has a low formaldehyde content of less than 100 ppm.
  • Especially suited for use in feminine hygiene and related absorbent products, and pre-moistened wipes.

General
VINNAPAS® eco 192 can be applied by a number of different application methods including saturation, spraying, foaming and print bonding.
It performs well on various fiber types including cellulose, rayon, glass and polyester. Temperatures above 150°C are necessary to achieve proper crosslinking.
 

Processing

Formulating recommendations include the addition of catalyst and a wetting surfactant. Catalysts should be added to the dispersion as a 10% solution under good agitation. Typical catalysts include ammonium chloride, citric acid and sodium bisulfate. A 1% catalyst level (solids on solids dispersion) is sufficient to achieve complete crosslinking of the polymer.
Surfactants can also be added to VINNAPAS® eco 192 to improve penetration of the binder into the substrate and improve absorbency of the finished product. Effective surfactant levels are 0.5 to 1.0% on dispersion solids. The compatibility and efficacy has to be checked undertaking a storage test.
 

Polymer Dispersions


VINNAPAS® eco 192 can be mixed with most VINNAPAS® and VINNOL® dispersions as well as with most anionic and/ or nonionic aqueous polymer dispersions. However the compatibility of the mixture should be tested by undertaking a storage test.


Defoaming Agents


Suitable defoaming agents include 1)SILFOAM® SE1662, 2) FOAMASTER® WO 2310, 3)AGITAN® 352 or 4)Surfynol® DF58.
The compatibility and efficiency should be tested in any case.

 


1) SILFOAM® is a trademark of Wacker Chemie AG
2) FOAMASTER® is a trademark of BASF SE
3) AGITAN® is a trademark of Münzing Chemie GmbH
4) SURFYNOL® is a trademark of Evonik Resource Efficiency GmbH

 

Thickening Agents
We recommend, in particular, products with neutral pH, e.g. those based on cellulose derivatives, polyvinyl alcohol or polyurethane. Should alkali-swellable polyacrylic acid derivatives be used those need to be chosen that are effective with ammonia, in order not to interfere with the acid catalyzed cross-linking of VINNAPAS® eco 192, like e.g. 5) Rheovis® AS1125, 6)Rheovis® AS1130, 7)ROHAGIT® SD15. Their compatibility and efficacy has to be checked.

 


5),6) RHEOVIS® is a trademark of BASF SE
7) ROHAGIT® is a trademark of Synthomer PLC

如果产品不是用于我们推荐的应用, 则购买者应对该产品的选择、加工和使用负全部责任. 此外还应遵守所有的相关法律法规.

Wacker Chemie AG

Hanns-Seidel-Platz 4

D-81737 Munich

Germany

储存

When the dispersion is stored in tanks, proper storage conditions must be maintained. The product has a shelf life of 6 months starting from the date of receipt if stored in the original, unopened containers at temperatures between 5 and 30 °C. Any longer periods for the maximum storage period that may be described in the Certificate of Analysis which accompanies each shipment of the product, take preference over this suggestion in which case the time period stated in the Certificate of Analysis shall be solely authoritative. Iron or galvanized iron containers and equipment are not recommended. Corrosion could result in discoloration of the dispersion or blends made from it in further processing. We therefore recommend the use of containers and equipment made of ceramic, rubberized or enameled materials, appropriately finished stainless steel, or plastic (rigid PVC, polyethylene or polyester resin). As polymer dispersions may tend to superficial film formation, skins or lumps may be formed during storage or transportation. A filtration process is thus recommended prior to utilization of the product.

Preservation for Transport, Storage and further Processing

The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package.

Measures should also be taken to ensure cleanliness of the tanks and pipes. In unstirred tanks, a layer of preservative-containing water should be sprayed onto the surface of the dispersion to prevent the formation of unwanted skin and possible attack by microorganisms. The thickness of this water layer should be < 5 mm for low viscosity dispersions and up to 10–20 mm for high viscosity products. Proper procedures – periodic tank cleaning and sanitization – must be set up in order to prevent microbial attack. Contact your biocide representative/supplier for further plant hygiene recommendations. Measures should be taken to ensure that only clean air enters the tank when the dispersion is removed.

Finished products manufactured from polymer dispersions usually also require preservation. The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required.

销售和支持

Changsha Port
长沙市开福区新港大道80号
000000 Changsha
中国大陆
+86  400  921-6699 (电话)
Contact Sales

我们可以为您提供什么帮助?

  • 您在选择产品方面需要帮助或者需要技术咨询? 请联系我们的专家
Ask a question

购物车

我的媒体


收藏夹

我的产品