ETONIS® 5210 P

ETONIS® 5210 P is a dispersion based on vinyl acetate and ethylene. It is produced without using formaldehyde donors and without adding plasticizers or organic solvents. The residual monomer content is below 1000 ppm.



特性

ETONIS® 5210 P exhibits a high compatibility towards cement and its influence on cement setting is marginal. It shows an excellent compatibility with inorganic fillers such as aggregates, sand and CaCO3 and imparts high bond strength combined with high flexural strength. Therefore, ETONIS® 5210 P offers several advantages in a wide range of concrete applications. For example, it can be used as polymer binder latex modified concrete (LMC), pre-fabricated concrete and primer for concrete etc. For latex modified concrete (LMC), ETONIS® 5210 P is compatible with other dispersions such as styrene/butadiene latex, styrene/acrylic and pure acrylic dispersions.

免责声明

所提供之所有信息均基于我们当前所掌握的知识。尽管如此,我们不对其作任何担保、也不承担任何责任,并且保留在任何时候进行技术变更的权利。购买方应在预测试中对所提供之信息以及产品在既定应用中的适应性进行检查。任何时候都必须以合同条款与条件为准。此外,本免责申明还适用于与第三方权利有关之事宜,尤其是在德国境外。

For further information regarding applications of ETONIS® 5210 P, refer to the section "application". Please discuss additional applications with your WACKER customer representative.

Processing:

ETONIS® 5210 P can be blended with most ETONIS® and VINNAPAS® dispersions and many other aqueous polymer dispersions in any ratio. When blending, it is important to adjust the pH of both dispersions which are to be blended in a pH range in which both dispersions are stable. Storage tests should be carried out to check the compatibility of the mixture.

包装

  • 1 KG BOTTLE
  • 1100 KG IBC

储存

When the dispersion is stored in tanks, proper storage conditions must be maintained. The product has a shelf life of 9 months starting from the date of manufacture if stored in the original, unopened containers at temperatures between 5 and 30°C. Any longer periods for the maximum storage period that may be described in the Certificate of Analysis which accompanies each shipment of the product, take preference over this suggestion in which case the time period stated in the Certificate of Analysis shall be solely authoritative. Iron or galvanized-iron equipment and containers are not recommended because the dispersion is slightly acidic. Corrosion may result in discoloration of the dispersion or its blends when further processed. Therefore, the use of containers and equipment made of ceramics, rubberized or enameled materials, appropriately finished stainless steel, or plastic (e.g. rigid PVC, polyethylene or polyester resin) is recommended. As polymer dispersions may tend to superficial film formation, skins or lumps may form during storage or transportation. Filtration is therefore recommended prior to utilization of the product.

Preservation for Transport, Storage and further Processing

The product is adequately preserved during transportation and storage if kept in the original, unopened containers. However, if it is transferred to storage tanks, the dispersion should be protected against microbial attack by adding a suitable preservative package. Measures should also be taken to ensure cleanliness of the tanks and pipes. In unstirred tanks, a layer of preservative-containing water should be sprayed onto the surface of the dispersion to prevent the formation of unwanted skin and possible attack by microorganisms. The thickness of this water layer should be < 5 mm for low viscosity dispersions and up to 10-20 mm for high viscosity products. Proper procedures - periodic tank cleaning and sanitization - must be set up in order to prevent microbial attack. Contact your biocide representative/supplier for further plant hygiene recommendations. Measures should be taken to ensure that only clean air enters the tank when the dispersion is removed. Finished products manufactured from polymer dispersions usually also require preservation. The type and scope of preservation will depend on the raw materials used and the anticipated sources of contamination. The compatibility with other components and the efficacy of the preservative should always be tested in the respective formulation. Preservative manufacturers will be able to advise you about the type and dosage of preservative required. If the product is stored for a long period, stirring is recommended before use.

销售和支持

Changsha Port
长沙市开福区新港大道80号
000000 Changsha
中国大陆
+86  400  921-6699 (电话)
Contact Sales

我们可以为您提供什么帮助?

  • 您在选择产品方面需要帮助或者需要技术咨询? 请联系我们的专家
Ask a question

您是否需要产品样本?

您可以在此处索取产品样本。

索取样本

更多产品

产品 技术数据
固体含量 动力粘度 密度 保护性胶体/乳化剂体系 与颜料和填料的相容性 玻璃化温度
ETONIS® 1400 S 46 - 48 % 46 - 48 % 200 - 800 mPa·s 200 - 800 mPa·s 1.06 - 1.08 g/cm³ 8.846 - 9.013 lb/gal - - - - - -
ETONIS® 1450 S - - 10 - 15 mPa·s 10 - 15 mPa·s 1.22 g/cm³ 10.181 lb/gal - - - - - -
ETONIS® 5150 P - - 100 - 400 mPa·s 100 - 400 mPa·s 大约 1.06 g/cm³ 大约 8.846 lb/gal - - - - - -
ETONIS® 5210 P 54 - 56 % 54 - 56 % 2700 - 3700 mPa·s 2700 - 3700 mPa·s - - 聚乙烯醇[1] 聚乙烯醇[1] Very good[2] Very good[2] 约 7 °C[3] 约 44.6 °F[3]
ETONIS® 7260 A - - 350 - 750 mPa·s 350 - 750 mPa·s 1.08 g/cm³ 9.013 lb/gal - - - - - -
说明
[1] 保护性胶体/乳化剂体系 | 专用方法,  [2] 与颜料和填料的相容性 | 专用方法,  [3] 玻璃化温度 | 专用方法 

购物车

我的媒体


收藏夹

我的产品