VINNAPAS® 4410 L
VINNAPAS® 4410 L is a dispersible polymer powder for dry mix mortars, specifically suited for self-leveling flooring compounds and screeds. It is based on a hard copolymer of vinylacetate and ethylene and belongs to the product class VINNAPAS® L which means that it improves the leveling and surface properties as well the stabilization of the fresh mortar. Cured mortars with VINNAPAS® 4410 L have improved adhesion, flexural strength, deformability and abrasion resistance.
- VINNAPAS® 4410 L is a copolymer powder of vinyl acetate and ethylene and is dispersible in water.
- As a polymeric binder VINNAPAS® 4410 L will provide very good workability to the fresh mortar.
- Cured mortars with VINNAPAS® 4410 L have improved adhesion, flexibility, flexural strength, deformability and abrasion resistance.
- VINNAPAS® 4410 L can be combined with casein or synthetic plasticizing admixtures to produce self-leveling flooring compounds and screeds.
- VINNAPAS® 4410 L produces very smooth surfaces that are free of surface voids.
- VINNAPAS® 4410 L contains a fine mineral filler as an antiblocking agent and is produced without the addition of organic solvents, plasticizers and film-forming agents.
- Special features of VINNAPAS® 4410 L are its very good defoaming properties even without additional defoamer in the mortar formulation. This results in exceptionally smooth, uniform surfaces without air bubbles while also offering high abrasion resistance, flexural and compressive strength. Furthermore it allows self-leveling flooring compounds to be formulated with a low content of volatile organic compounds (VOC). The product thus can be used to produce self-leveling flooring compounds conforming to strict eco-labeling requirements.
VINNAPAS® 4410 L的特殊性能
For typical application fields of VINNAPAS® 4410 L, refer to the section "application". Please discuss additional applications with your WACKER customer representative.
For the production of ready-mixed dry mortars, such as adhesives and patching compounds, blend VINNAPAS® 4410 L with the other dry ingredients in appropriate equipment. Temperatures should not be allowed to rise excessively during mixing because otherwise the dispersible polymer powder could agglomerate by virtue of its thermoplastic properties. The mortar is prepared for use by adding the recommended amount of water and mixing mechanically or by hand. Since hand mixing generates little shear force, we recommend allowing the fresh mortar to slake for 5 minutes and then stirring it again. This is usually unnecessary where mechanical mixers are employed.
如果产品不是用于我们推荐的应用, 则购买者应对该产品的选择、加工和使用负全部责任. 此外还应遵守所有的相关法律法规.
Big Bags or bulk on request.