WACKER® CATALYST T 79

WACKER® CATALYST T 79 is the standard curing agent for the WACKER silicone rubber ELASTOSIL® RT 779. The shear-thinning paste provides excellent adhesion properties and improves the oil resistance of ELASTOSIL® RT 779.



特性

  • Non-slump paste
  • To be processed with base compound ELASTOSIL® RT 779 (recommended mixing ratio: 10:1)
  • Very fast curing at room temperature
  • Curing speed tunable by mixing ratio
  • Provides excellent adhesion to many substrates (glass, ceramics, wood, metals, plastics and powder coatings)

WACKER® CATALYST T 79的特殊性能

  • 剪切变稀
  • 稳定固化
  • 缩合固化
  • 自粘性
  • 触变

免责声明

所提供之所有信息均基于我们当前所掌握的知识。尽管如此,我们不对其作任何担保、也不承担任何责任,并且保留在任何时候进行技术变更的权利。购买方应在预测试中对所提供之信息以及产品在既定应用中的适应性进行检查。任何时候都必须以合同条款与条件为准。此外,本免责申明还适用于与第三方权利有关之事宜,尤其是在德国境外。

  • Curing agent for condensation curing RTV-2 silicone rubber ELASTOSIL® RT 779
  • Typical fields of application: automotive, mechanical engineering.

WACKER® CATALYST T 79 is used as standard curing agent for the base compound ELASTOSIL® RT 779. The shear-thinning paste provides excellent adhesion properties and improves oil resistance.

 

The crosslinking reaction of condensation curing RTV-2 silicones is relatively robust in regard to curing inhibition. Amine containing materials, urethanes, organic compounds with sulfur-containing groups, organometallic compounds, plasticizers, lubricants, oils and grease usually do not impair the curing process itself. Nevertheless, for optimum adhesion results all substrates used should be clean, dry and free from grease, waxes, dust or other surface contaminations.

 

Mixing and curing:

To ensure uniform curing both components (i.e. rubber base ELASTOSIL® RT 779 and curing agent WACKER® CATALYST T 79) have to be thoroughly mixed, either manually or by automatic metering lines equipped with static or dynamic mixing devices. The recommended mixing ratio is 10:1 by weight.

 

Potlife and curing speed can be modified within limits by adjusting the ratio of base compound to curing agent. Varying the mixing ratio between 8:1 and 12:1 usually has a small effect on the properties of the cured rubber. However, if the mixing ratio differs substantially from the recommended scope, preliminary tests should be carried out to check the cured material’s suitability. General information about pot life and resulting curing times is given in the table "Catalyzed".

 

Moreover curing speed can be slightly accelerated by raising the temperature. Heating, however, must not exceed 60 °C before curing is completed.

 

After completion of the vulcanization process the product may continuously be exposed to constantly changing climatic conditions, UV radiation and high temperature without damage. ELASTOSIL® RT 779, cured with WACKER® CATALYST T 79, usually shows good primerless adhesion to many substrates, even when continuously exposed to motor oil and lubricants.

 

Removal:

If removal of silicone rubber from machines or dispensing equipment is necessary, white spirit or similar nonpolar solvents are recommended. However, cleaning ideally should take place before the silicone is fully vulcanized. Cured silicone rubber needs to be removed mechanically, if necessary in combination with a swelling agent (solvent).

 

Detailed information about processing RTV-2 silicones is given in our brochure “ROOM TEMPERATURE VULCANIZING (RTV) SILICONES - MATERIAL AND PROCESSING GUIDELINES”. We recommend running preliminary tests to optimize conditions for the particular application.

储存

Store in a dry and cool place.

 

The 'Best use before end' date of each batch is shown on the product label.

 

Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

销售和支持

Wacker Chemicals (China) Co.,Ltd.
Caohejing Hi-Tech Park
200233 Shanghai
中国
+86  21  6130-2000 (电话)
+86 21 6130-2500  (传真)
Contact Sales
网站

我们可以为您提供什么帮助?

    您在选择产品方面需要帮助或者需要技术咨询? 请联系我们的专家
Ask a question

您是否需要产品样本?

您可以在此处索取产品样本。

索取样本

更多产品

没有找到类似的产品