SILRES® BS 710

SILRES® BS 710 is a permanent anti-graffiti coating for the protection of concrete, masonry, wood and pre-existing coatings. It is based on polyorganosiloxanes and provides excellent performance against exterior elements such as rain, sun and temperature extremes. SILRES® BS 710 is a single component product, that cures at room temperature with ambient moisture. The cured coating provides excellent release and ease of removal of most permanent markers and aerosol paints.



特性

SILRES® BS 710 contains a select mixture of silicone compounds. The relatively high molecular weight silicone ingredients react with moisture under formation of the anti-graffiti coating with an excellent adhesion to the host surface. Thereby it is improving its weathering resistance and breathability.

  • One-component system
  • effective on many building materials
  • single layer application usually sufficient, multi layer application possible
  • weatherproof
  • water repellent
  • permeable to water vapor
  • solvent dilutable and environmentally compatible
  • Graffiti removal with water
  • enhances the colour of the surface

免责声明

所提供之所有信息均基于我们当前所掌握的知识。尽管如此,我们不对其作任何担保、也不承担任何责任,并且保留在任何时候进行技术变更的权利。购买方应在预测试中对所提供之信息以及产品在既定应用中的适应性进行检查。任何时候都必须以合同条款与条件为准。此外,本免责申明还适用于与第三方权利有关之事宜,尤其是在德国境外。

Particularly suitable for mineral building materials such as concrete, brick, limesandstone, natural and artificial stone, plaster, wood and coated metal surfaces as a permanent protection against graffiti. SILRES® BS 710 is to use only after a thorough examination on coated metal and plastic surfaces and possibly in combination with a suitable primer.

Processing

Apply SILRES® BS 710 to a clean dry surface. Surface may be cleaned by scrubbing or power washing with a common solvent or cleaner. SILRES® BS 710 can be thinned to the desired application viscosity. Aliphatic solvents are the preferred choice. Other solvents may be used however all combinations must be tested to ensure clarity of the coating, solvency and stability. Weak solvent combinations can lead to a loss of cure, clarity or even precipitation of the coating’s solids. For this reason methyl acetate is not recommended.

SILRES® BS 710 is applied using an airless sprayer. However, brush or roller are also suitable methods of application for small surface areas. Primer is not needed prior to SILRES® BS 710 to most common surfaces. Due to it’s consistency SILRES® BS 710 is easy to be applied in a single coat.

A test area should be applied especially on painted or existing graffiti surfaces.

With proper protective equipment SILRES® BS 710 may be applied via industrial spray application methods such as airless and conventional spray. See SDS for proper protective equipment. After use, the spray equipment and lines must immediately be flushed with solvents to prevent the coating from curing and forming a tough adherent cured film.

SILRES® BS 710 cures quickly once applied to dry substrates and exposed to humidity in the air. Curing occurs at the surface and progresses to the substrate based on the available ambient moisture. Complete drying for heavier film builds may require up to 24 hours.

Containers, once opened, should be used until empty. Any remaining coating, exposed to air will continue to cure and thicken resulting in surface skinning and increased viscosity.

储存

The 'Best use before end' date of each batch is shown on the product label.

Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

销售和支持

Wacker Chemicals (China) Co.,Ltd.
Caohejing Hi-Tech Park
200233 Shanghai
中国
+86  21  6130-2000 (电话)
+86 21 6130-2500  (传真)
Contact Sales
网站

我们可以为您提供什么帮助?

    您在选择产品方面需要帮助或者需要技术咨询? 请联系我们的专家
Ask a question

更多产品

请选择一个应用程序查看您的产品匹配。