SILRES® H62 C

SILRES® H62 C is a liquid, solvent-free one-part heat-curing phenyl silicone resin formulation. The product is ideal to impregnate electrical coils of motors and generators. Besides SILRES® H62 C can be used to provide hydrophobic properties to porous materials and as binder for composites made of fibrous fillers, cloths, woven or non-woven reinforcing materials.

 

The formulation is ready-to-use and crosslinks under heat. While curing SILRES® H62 C does not release chemical byproducts, and hence a curing shrink is barely noticeable. The product also thermosets in thick layers, even when in contact with air.

 

Fully cured SILRES® H62 C has excellent electrical insulation properties and outstanding long-term heat resistance. It additionally shows high stability against weathering, moisture and UV light, and it can therefore be exposed continuously to constantly changing climatic conditions or UV radiation.



特性

Uncured:

  • Liquid, solvent-free formulation
  • Based on silicone resins with phenyl and methyl groups
  • Very low content of volatiles
  • Optimized for vacuum pressure impregnation (VPI)
  • To a certain degree also suitable for dipping and trickling impregnation
  • Can be processed at temperatures up to a maximum of 80 °C to reduce viscosity
  • Cures with almost no evolution of heat
  • Recommended curing temperature for fast thermosetting: above 160 °C

 

Cured:

  • Tack-free
  • Excellent long-term heat stability (RTI: 239 °C)
  • meets the requirements of insulation class N and R (DIN EN 60085), i.e. former insulation class C
  • Conforms to the fire safety requirements defined in UL 94 V-0.

SILRES® H62 C的特殊性能

  • 不含溶剂
  • 与颜料和填料的相容性
  • 低粘度
  • 加成固化
  • 单组分
  • 单组分热固化
  • 即用型
  • 可实现出色的憎水性
  • 憎水性
  • 抗潮湿
  • 液体
  • 电绝缘性
  • 硬度高(邵氏D级)
  • 耐热性
  • 耐电痕性和腐蚀性
  • 耐紫外线性和耐候性

免责声明

所提供之所有信息均基于我们当前所掌握的知识。尽管如此,我们不对其作任何担保、也不承担任何责任,并且保留在任何时候进行技术变更的权利。购买方应在预测试中对所提供之信息以及产品在既定应用中的适应性进行检查。任何时候都必须以合同条款与条件为准。此外,本免责申明还适用于与第三方权利有关之事宜,尤其是在德国境外。

  • Impregnation agent for electrical coils and for porous materials
  • Binder for laminates made of fibrous fillers, cloths, woven or non-woven reinforcing materials
  • Typical fields of industrial applications: household appliances, mechanical engineering, automotive, electrical industry, railway industry

 

SILRES® H62 C is supplied as a ready-to-use formulation. The materials to be treated should be clean and free of dirt, rust, oil or grease. Though the 1-part heat-curing formulation is remarkable insensitive to curing inhibitors, it is recommended to run a small-scale test in order to check for each substrate’s ability to inhibit cure. Examples of potentially inhibiting contaminants are sulfur containing materials, plasticizers, urethanes, amine containing materials and organometallic compounds – especially organotin compounds.

 

The curing time of SILRES® H62 C is highly dependent on temperature and on both the size and the heat sink properties of the parts being treated. The product is usually cured between 160 °C and 210 °C in order to secure a fast setting. Typical curing temperatures and resulting curing times are given in adjacent table.

 

1. Impregnation of Electrical Coils:

Due to its excellent electrical insulation properties and outstanding long-term heat resistance SILRES® H62 C is used for the impregnation of electrical coils in traction motors, electric drives and smoke-extraction motors. The silicone resin formulation is usually processed by vacuum pressure impregnation (VPI). However it is also possible to apply SILRES® H62 C by dipping and trickling.

 

Please note: impregnating electrical coils is a complex process that needs a thorough control of various process parameters, such as pre-heating the coils, the viscosity and condition of the impregnation agent, impregnation temperature, curing temperature, heating rate and temperature ramp, and other production line specific conditions. Therefore, the following indications are inteded as a guide only, and we recommend running preliminary tests to optimize the conditions of the particular process.

 

The following sequence illustrates a typical standard VPI process:

 

1. The electrical coil is dried inside the impregnation vessel at elevated temperature and under vacuum (0.5 - 5 mbar).

2. The impregnation vessel - still under vacuum - is then filled with SILRES® H62 C to completely cover the electrical coils.

3. To accelerate impregnation speed, pressure is applied (2 - 5 bar) until impregnation is complete.

4. After draining the vessel excessive impregnation agent is allowed to drip off.

5. Finally the coils are transfered into a circulating air oven; typical curing conditions: 200°C, 12 hours, ideally under continuous rotation of the impregnated coils to secure a uniform silicone resin distribution inside the coil and to minimize drip off loss.

 

Important: in order to minimize the risk of crack formation due to the differing thermal expansion of the coil materials, the thickness of cured SILRES® H62 C should not significantly exceed 100 μm.

 

For further details, please revert to our brochure "SILRES® H62 C - IMPREGNATING RESIN FOR VACUUM PRESSURE IMPREGNATION (VPI)".

 

 

2. Composites Based on Fibres or Cloths

Since fully cured SILRES® H62 C provides water repellency, excellent electrical insulation properties, outstanding heat resistance and long term stability against weathering, moisture and UV light, the product can be used as a binder for composites based on fibres, cloths, woven or non-woven reinforcing materials. Besides it is possible to pyrolyze the respective composite materials at high temperature in order to obtain cohesively very strong composite ceramics.

 

Please note: best results are obtained with fabrics that are made from non-sized fibres or from fibres with epoxy-functional sizing agents.

 

For the manufacture of layered composites (e.g. based on glass fibre, carbon fibre, mineral fibre or stone fibre) the cloth or the fibre strand is impregnated with SILRES® H62 C either by spraying, or by running the reinforcing material through an impregnation bath. If necessary, the impregnation resin can be warmed to 60 °C prior use in order to improve penetration speed. Depending on the target shape of the laminate the wet fabric or fibre strand either is rolled-up in layers, or it is cut up into smaller pieces which in turn can be sandwiched, e.g. into a shaped press mold or as a flat fabric stack. Curing for 4 hours at high temperature (200 °C) and, if applicable, high pressure (e.g. 10 bar) gives the respective composite structure.

 

 

3. Hydrophobic Sealing of Tubular Heating Elements

Fully cured SILRES® H62 C provides high water repellency, excellent electrical insulation properties and outstanding heat resistance. It is therefore often used in combination with silicone rubber (e.g. ELASTOSIL® N 288, ELASTOSIL® E 10, ELASTOSIL® A 234 or ELASTOSIL® RT 706) for the hydrophobic sealing of tubular heating elements.

 

For this purpose the tubes ends are charged with a few milliliters of SILRES® H62 C after the tube has been equipped with the heating wire and filled with magnesium oxide powder that acts as heat transfer medium and as dielectric packing material for the wire. The liquid silicone resin formulation SILRES® H62 C impregnates the filler particles within a zone of a few millimeters and thus provides a durable moisture barrier after curing at the first heating cycle.

储存

Store in a dry and cool place.

 

The 'Best use before end' date of each batch is shown on the product label.

 

Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.

销售和支持

Wacker Chemicals (China) Co.,Ltd.
Caohejing Hi-Tech Park
200233 Shanghai
中国
+86  21  6130-2000 (电话)
+86 21 6130-2500  (传真)
Contact Sales
网站

我们可以为您提供什么帮助?

    您在选择产品方面需要帮助或者需要技术咨询? 请联系我们的专家
Ask a question

您是否需要产品样本?

您可以在此处索取产品样本。

索取样本

更多产品

请选择一个应用程序查看您的产品匹配。