SILPURAN® 2110 A/B
Two-component, addition-curing silicone composition curing to a soft silicone adhesive
- biocompatible, certificates of compatibility with USP Class VI and ISO 10993 available on request
- no by-products from curing process
- medium viscosity, pourable
- mixing ratio 1 : 1
- good adhesion, typical value 2.1 N/2.5 cm (90° peel test, on stainless steel)
- high transparency
All the information provided is in accordance with the present state of our knowledge. Nonetheless, we disclaim any warranty or liability whatsoever and reserve the right, at any time, to effect technical alterations. The information provided, as well as the product's fitness for an intended application, should be checked by the buyer in preliminary trials. Contractual terms and conditions always take precedence. This disclaimer of warranty and liability also applies particularly in foreign countries with respect to third parties' rights.
SILPURAN® 2110 A/B can be used as a skin adhesive in medical applications.
Components A and B of SILPURAN® 2110 A/B are mixed homogeneously in a ratio A : B = 1 : 1 and vulcanise rapidly at temperatures over 100 °C.
SILPURAN® 2110 A/B has good adhesive properties that can be adjusted to suit the relevant requirements:
Increasing the proportion of component A results in a softer vulcanisate and increased tackiness. Increasing the proportion of component B results in a harder vulcanisate and reduced tackiness.
The platinum catalyst is contained in component A.
Only A and B components with the same batch number may be processed together!
The 'Best use before end' date of each batch is shown on the product label.
Storage beyond the date specified on the label does not necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.
Sales and support
How can we help you?
- Do you need help in choosing a product or do you require technical support? If so, please contact our experts.
Would you like a product sample?
You can request a product sample here.Request sample
|SILPURAN® 2100 A/B||34000 mPa·s 34000 mPa·s||205 1/10mm 205 1/10mm|
|SILPURAN® 2110 A/B||54000 mPa·s 54000 mPa·s||200 1/10mm 200 1/10mm|
|SILPURAN® 2112 A/B||11600 mPa·s 11600 mPa·s||225 1/10mm -|
|SILPURAN® 2114 A/B||12000 mPa·s 12000 mPa·s||200 1/10mm 200 1/10mm|
|SILPURAN® 2117 A/B||33000 mPa·s 33000 mPa·s||205 1/10mm -|
|SILPURAN® 2120 A/B||31000 mPa·s 31000 mPa·s||120 1/10mm -|
|SILPURAN® 2122 A/B||2500 mPa·s 2500 mPa·s||180 1/10mm -|
|SILPURAN® 2130 A/B||1000 mPa·s 1000 mPa·s||220 1/10mm 220 1/10mm|
 Viscosity, dynamic | DIN EN ISO 3219,  Penetration | DIN ISO 2137 | hollow cone of 62.5 g, 60 s, curing time 60 min at 120 °C,  Penetration | DIN ISO 2137 | hollow cone of 62.5 g, 60 s, curing conditions 60 min at 120 °C,  Penetration | DIN ISO 2137 | (hollow cone of 62.5 g, 60 s, curing time 60 min at 120 °C,  Penetration | hollow cone of 62.5 g, curing time 60 min at 120 °C,  Penetration | hollow cone of 62.5 g, 60 s, curing time 60 min at 120 °C