SEMICOSIL® 912

SEMICOSIL® 912 is a pourable, addition-curing, 2-part silicone rubber that cures to a soft silicone gel when mixed with ELASTOSIL® CAT PT, ELASTOSIL® CAT PT-F or ELASTOSIL® CAT UV.



Eigenschaften

  •  two-part, 10 : 1 mixing ratio
  •  low viscosity
  •  modular system allows flexible adjustment of pot life and curing time by selection among different catalysts (no lot binding between base and catalyst)
  •  fast curing at room temperature with Catalyst PT-F
  •  long pot life at room temperature with Catalyst PT
  •  extremely fast curing with Catalyst UV
  •  low hardness
  •  excellent tackiness

Disclaimer

Alle unsere Angaben beruhen auf bestem Wissen. Allerdings übernehmen wir hierfür keine Haftung oder Gewährleistung und behalten uns jederzeit technische Änderungen vor. Es liegt in der eigenen Verantwortung des Käufers, die Angaben sowie die Geeignetheit unseres Produktes für den vorgesehenen Einsatzzweck vor dem Gebrauch zu überprüfen. Vertragliche Regelungen gehen immer vor. Der Gewährleistungs- und Haftungsausschluss gilt - insbesondere im Ausland - auch im Hinblick auf Schutzrechte Dritter.

Datenblätter

Encapsulation of electronic components for the automotive and power electronics industries.

Surface preparation
All surfaces must be clean and free of contaminants that will inhibit the cure of the product. Examples of inhibiting contaminants are sulfur containing materials, plasticizers, urethanes, amine containing materials and organometallic compounds – especially organotin compounds.

Mixing
The product contains the crosslinker, ELASTOSIL® CAT PT, PT-F or UV contains the catalyst. Even traces of catalyst may cause gelling of the component containing the crosslinker. Therefore tools (spatula, stirrers, etc.) used for handling the catalyst-containing component or the catalyzed compound must not come into contact with this component.

The two components should be thoroughly mixed at a 10 : 1 ratio by weight or volume. To eliminate any air introduced during dispensing or trapped under components or devices a vacuum encapsulation is recommended.

Curing
For curing an oven at elevated temperatures can be used.

Oven temperature                      Curing time
100°C                                         2 mm

Catalyst PT                                30 min
Catalyst PT-F                             10 min
Catalyst UV                                2 min
# UV dose 1.5 J/cm2, 250-350nm

The system is activated by direct UV irradiation. UV-irradiation should use emissions in the wavelength range between 250 and 350 nm.
Typically D-bulbs (Fe-doped, Hg-light sources) using ozone-free quartz should be used and are commercially available (see figure 2). H-bulbs with emissions below 250 nm are not recommended.

Curing time of the UV-active system is highly dependent both on the intensity and dose of the UV-light and the spectral intensity distribution. The curing is also dependent on the layer thickness, the optical properties of the substrate and temperature. Increase of the temperature will fasten curing reaction.

Lagerung

Das Mindesthaltbarkeitsdatum der jeweiligen Charge ist auf dem Produktetikett angegeben. Eine Lagerung über den auf dem Produktetikett angegebenen Zeitraum hinaus bedeutet nicht notwendigerweise, dass die Ware unbrauchbar ist. Eine Überprüfung der für den jeweiligen Einsatzzweck erforderlichen Eigenschaftswerte ist jedoch in diesem Falle aus Gründen der Qualitätssicherung unerlässlich.

Vertrieb & Support

Wacker Chemie AG
Heilbronner Strasse 74
70191 Stuttgart
Deutschland
+49  711  61942-0 (Phone)
+49 711 61942-61  (Fax)
Kontakt

Wie können wir Ihnen helfen?

  • Benötigen Sie Unterstützung bei der Produktauswahl oder wünschen Sie eine technische Beratung? Kontaktieren Sie unsere Experten.
Frage stellen

Sie möchten ein Produktmuster?

Hier können Sie ein Produktmuster anfordern.

Muster anfordern

Bestellen

Meine Medien


Meine Favoriten

Meine Produkte